Leader Clipperlon 2130
Description
Homogeneous expanded PTFE sheet, which uses product geometry rather than fillers or binders to address concerns associated with traditional PTFE material
Downloads
Product Data SheetApplication
2130 is designed for oxidizing application, harsh chemical environments and areas where contamination is a problem. 2130 is completely chemically inert and is suitable for sealing all chemicals across the pH range with the exception of molten alkali metals and fluorine gas.
Advtantages
Clipperlon 2130 achieves very good stability and tightness with good blow-out resistance especially in demanding steel flange applications. The good resistance behaviour of the material leads to increased operating safety, even in changing operating conditions.
Chemical Compatiblity
Patricularly suitable for use with hydrofluoric acid, but not pure hydrogen fluoride. Best for use with string alkalis, solvents, fuels, water, steam and chlorine. Other applications include solvents, fuels, water, oil, chlorine and caustics. A chemical resistance listis available upon request.
Delivery Options
Flange gaskets and sheets are available in thickness of 1/32",1/16", 1/8", 0,5mm, 1mm, 1,5mm, 2mm and 3mm. Other thicknesses available on request.. Standard gaskets can be supplied in accordance with ASME B16.21, EN12560-1 as well as EN1514-1. Non-standard or special gaskets can be manufactured according to customer drawings, or by given sizes or Edrawing.
Temperature
Particularly suitable for temperature from – 240 ° up to 260 °C.
Approvals
- FDA 21 CFR 177.1550
- TA-Luft
- EC1935 (10/2011)
Certificates
- TA-Luft
Sealing Characteristics
- excellent sealability
- non ageing
- low leak rate
- good electrical insulation properties
- outstanding chemical resistance
max Temperature [°C] | 260 |
min Temperature [°C] | -240 |
max Pressure [bar] | 40 |
density [g/cm3] | 0.8 |
Leakage Specific Leak Rate [DIN 28090-2] [mg/(s*m)] | 0.01 |
Minimum initial stress [DIN E 2505 part 2] [N/mm2] | 25 |
Maximum initial stress [DIN E 2505 part 2] [N/mm2] | 160 |
M-Value | 2.5 |
Y- Value [psi] | 2900 |
min Seating stress [Qmin(L 0,01), mg/(s*m)] at RT 40 bar [N/mm2] | 27 |
ASTM F36 Recovery [% min] | 12 |
Gasket required flange roughness [Ra micron] | 3,2-6,3 |
Gasket required flange roughness [RMS] | 125-250 |
max Seating stress [Qsmax bei RT EN13555] [n/mm2] | 230 |
Relaxation PQR (30 MPA 150°C) [%] | 0.42 |
Residual seating stress , [QA=40 MPA,Qmin(L 0,01), mg/(s*m)] bei RT 40 bar [N/mm2] | 10 |
ROTT [Gb] | 1259 |
ROTT [a] | 0.202 |
ROTT [Gs"] | 3.58 |